Increasing the Elastic Modulus of Graphene by Controlled defect Creation

Article: published in Nature Physics by Cristina Gómez-Navarro and Julio Gómez-Herrero, IFIMAC researchers and members of the Department of Condensed Matter Physics.

The extraordinary strength, stiffness and lightness of graphene have generated great expectations of its application in flexible electro nics and as a mechanical reinforcement agent. However, the presence of lattice defects, un avoidable in sheets obtained by scalable routes, might degrade its mechanical properties. Here we report a systematic study on the elastic modulus and strength of graphene with a controlled density of defects. Counter-intuitively, the in-plane Young’s modulus increases with increasing defect density up to almost twice the initial value for a vacancy content of ~0.2%. For a higher density of vacancies, the elastic modulus decreases with defect inclusions. The initial increase in Young’s modulus is explained in terms of a dependence of the elastic coefficients on the momentum of flexural modes predicted for two-dimensional membranes. In contrast, the fracture strength decreases with defect density according to standard fracture continuum models. These quantitative structure–property relationships, measured in atmospheric conditions, are of fundamental and technological relevance and provide guidance for applications in which graphene mechanics represents a disruptive improvement. [Full article]

Share this article